Di seguito sono riportati i dati relativi alle prove di fatica svolte.
A.1 Dati prove di fatica tensile-shear
I dati sono stati ottenuti con carico variabile sinusoidalmente alla frequenza di 4 Hz
e rapporto di carico R = Pmin/Pmax = 0.1.
Provino N d [mm] Pmax [N] τ[MPa] max σ[MPa] Scr(max) Note
S1c/01 549000 - 2109 52.7 647.3 - S1c/02 770000 2 2109 52.7 647.3 (N) S1c/03 - - - Rotto staticamente. S1c/04 5000000 - 1668 41.7 511.8 Run-out S1c/05 2535000 3 2109 52.7 647.3 (N) S1c/06 498700 2 2354 58.9 722.6 (N) S1c/07 430000 2.5 2354 58.9 722.6 (N) S1c/08 470000 2 2158 54.0 662.4 (N) S1c/09 795000 4 1864 46.6 572.0 (N) S1c/10 1085000 2 1864 46.6 572.0 (N) S1c/11 908000 2.5 1962 49.1 602.1 (N) S1c/12 1100000 2 1766 44.1 541.9 (N) S1c/13 1192200 3 1717 42.9 526.9 (N) S1c/14 751200 - 1717 42.9 526.9 Rotto staticamente. S1p/01 - - 2354 58.9 722.6 Rotto staticamente. S1p/02 676200 7 2354 58.9 722.6 (P) S1p/03 656200 5 2453 61.3 752.7 (P) S1p/04 987500 4.5 1962 49.1 602.1 (P) e (N) S1p/05 - - 2158 54.0 662.4 Rotto staticamente.
Tabella A-1 − Prova di fatica tensile-shear provino S1 (saldatura a tratto), criterio di fatica: d = 2÷4
Provino N Pmax [N] τmax [MPa] σScr(max) [MPa] Note S1c/01 690700 2109 52.7 647.3 S1c/02 2403300 2109 52.7 647.3 S1c/05 4111600 2109 52.7 647.3 S1c/11 2195200 1962 49.1 602.1 S1c/12 2330600 1766 44.1 541.9
Tabella A-2 − Prova di fatica tensile-shear provino S1 (saldatura a tratto), rottura completa. Provino N d [mm] Pmax [N] τ[MPa] max σ[MPa] Scr(max) Note
S2c/01 890000 - 2158 54.0 662.4 S2c/02 790000 18 2158 54.0 662.4 (N) S2c/03 1817000 8 1668 41.7 511.8 (N) S2c/04 2546000 15 1668 41.7 511.8 (P) S2c/05 5900000 - 1472 36.8 451.6 Run-out S2c/06 398000 12 2354 58.9 722.6 (P) e (N). S2c/07 392000 9 2158 54.0 662.4 (P) S2c/08 - - 1864 46.6 572.0 Rotto staticamente. S2c/09 1045600 14 1864 46.6 572.0 (N) S2c/10 702500 11 1962 49.1 602.1 (P) S2c/11 777000 11 1962 49.1 602.1 (N) S2c/12 2652600 - 1570 39.2 481.7 Rotto staticamente. Nessuna cricca rilevata.
S2c/13 - - 1570 39.2 481.7 Rotto staticamente.
S2c/14 - - 1570 39.2 481.7 Rotto staticamente.
S2p/01 418000 10 2354 58.9 722.6 (N)
S2p/02 475700 12 2453 61.3 752.7 (N)
S2p/03 689900 11 1962 49.1 602.1 (N)
Tabella A-3 − Prova di fatica tensile-shear provino S2 (saldatura ad anello), criterio di fatica: 8÷12 mm.
(P) → cricca sulla faccia penetrata dal laser, (N) → faccia non penetrata.
Provino N Pmax [N] τmax [MPa] σScr(max) [MPa] Note
S2c/01 956600 2158 54.0 662.4
S2c/02 856700 2158 54.0 662.4
S2c/03 2521400 1668 41.7 511.8
A.2 Dati prove di fatica di trazione pura
I dati sono ottenuti con carico variabile sinusoidalmente tra Pmin = 1000 N e Pmax
alla frequenza di 10 Hz.
Provino N R Pmax [N] σmax [MPa] Note
T0/1 232300 0.04 25506 340.1 T0/2 5245600 0.04 23544 313.9 Run-out T0/3 132900 0.04 27468 366.2 T0/4 225500 0.04 25506 340.1 T0/5 4500000 0.04 23544 313.9 Run-out T0/8 157900 0.04 26487 353.2
Tabella A-5 − Prova di fatica di trazione pura provino T0 (materiale base).
Provino N R Pmax [N] σmax [MPa] Note
T1/01 5372500 0.03 33354 222.4 Run-out.
T1/02 5850000 0.03 38259 255.1 Run-out.
T1/03 595400 0.02 44145 294.3
T1/04 4683100 0.02 43164 287.8 Run-out.
T1/05 516000 0.02 47088 313.9 Rottura materiale base. T1/06 890700 0.02 43164 287.8
T1/07 4331400 0.02 41202 274.7 Run-out.
T1/08 450000 0.02 47088 313.9
T1/09 436900 0.02 44145 294.3 Rottura materiale base.
T1/10 5420000 0.02 41202 274.7 Run-out.
Tabella A-6 − Prova di fatica di trazione pura provino T1 (saldatura longitudinale). Provino N R Pmax [N] σmax [MPa] Note
T2/1 1935400 0.03 30411 202.7 Rottura materiale base. T2/2 7395500 0.04 25506 170.0 Run-out.
T2/3 2825200 0.03 30411 202.7 Rottura materiale base. T2/4 1987700 0.03 33354 222.4 Rottura materiale base.
T2/5 450000 0.04 27468 183.1 Forte distorsione angolare residua. T2/6 6560000 0.03 33354 222.4 Run-out.
A.3 Dati prove di fatica pannelli
I dati sono ottenuti con carico variabile sinusoidalmente a frequenza di 4 Hz con
P
min = 2 kN. Nm è la media dei numeri di cicli a rottura delle singole cricche appartenential pannello.
Pannello Pmax [kN] R Nm Note
P1 19.6 0.10 (5000000) Run-out.
P2 35.3 0.06 550000 P3 31.4 0.06 859000 P4 25.5 0.08 1856000 P5 22.6 0.09 3215000
P6 31.4 0.06 1300000 Pelle tesa: sald. passante. P7 35.3 0.06 (2300000) Saldatura continua. Run-out. Tabella A-8 − Carico massimo applicato ai pannelli.
N. Linea sald. X [mm] N d [mm] σScr(max) [MPa] 1 1 301 695000 3 374.0 2 1 240 520000 2 406.4 3 1 179 695000 2 344.9 4 1 345 695000 2 351.1 5 1 285 520000 2 381.8 6 1 225 520000 2 409.6 7 2 281 520000 2 383.8 8 2 220 520000 2 408.7 9 2 305 695000 3 372.1 10 2 245 520000 2 404.0 11 3 361 695000 2 340.4 12 3 301 250000 2 374.0 13 3 239 400000 2 406.8 14 3 179 520000 2 344.9 15 3 346 695000 2 350.5 16 3 285 695000 2 381.8 17 3 225 520000 2 409.6 18 4 303 520000 2 373.1 19 4 243 520000 2 405.0 20 4 183 695000 <2 355.5 21 5 364 520000 2 338.2 22 5 307 350000 2 371.2 23 5 246 225000 2 403.4 24 5 181 520000 2 350.2 25 5 345 695000 2 351.1
N. Linea sald. X [mm] N d [mm] σScr(max) [MPa] 28 5 165 695000 2 304.5 29 6 341 520000 2 353.5 30 6 280 350000 2 384.3 31 6 220 350000 2 408.7 32 6 159 695000 2 286.7 33 6 365 695000 2 337.4 34 6 304 520000 2 372.6 35 6 244 520000 2 404.5 36 6 184 695000 2 358.0 Tabella A-9 − Prova di fatica pannello P2.
N. Linea sald. X [mm] N d [mm] σScr(max) [MPa] 37 1 360 1026000 2 303.2 38 1 298 1026000 2 333.7 39 1 346 1026000 3 311.5 40 1 286 634000 <2 338.9 41 2 348 1026000 2 310.4 42 2 297 960000 3 334.2 43 2 245 750000 2 359.1 44 2 195 750000 2 340.1 45 2 144 680000 2 217.1 46 2 290 800000 2 337.2 47 2 240 650000 2 361.2 48 2 190 960000 3 330.9 49 3 297 1026000 2.5 334.2 50 3 237 925000 2 362.3 51 3 176 1026000 2 299.2 52 3 348 960000 2 310.4 53 3 288 634000 <2 338.0 54 3 228 634000 3 364.0 55 4 340 1026000 2 314.7 56 4 278 1026000 5 342.5 57 4 218 875000 2 362.7 58 4 367 1026000 2 298.6 59 4 307 680000 2 329.9 60 4 247 634000 2 358.1 61 4 182 960000 - 313.7 62 5 298 634000 <2 333.7 63 5 238 634000 2 361.9 64 5 177 960000 3 301.7 65 5 343 960000 2 313.1 66 5 285 680000 2 339.3 67 5 225 634000 2 364.1 68 6 340 1026000 2 314.7 69 6 280 960000 2 341.6 70 6 220 825000 2 363.3
N. Linea sald. X [mm] N d [mm] σScr(max) [MPa] 73 6 245 500000 2 359.1 74 6 185 960000 - 320.4 75 6 240 960000 2 361.2 76 6 285 960000 - 339.3 77 6 225 960000 - 364.1 Tabella A-10 − Prova di fatica pannello P3.
N. Linea sald. X [mm] N d [mm] σScr(max) [MPa] 78 1 365 2362000 <2 243.7 79 1 304 1600000 2 269.1 80 1 244 1500000 2 292.1 81 1 340 2070000 <2 255.7 82 1 280 1382000 2 277.5 83 1 219 1382000 <2 295.0 84 2 347 2362000 2 252.7 85 2 286 1382000 2 275.4 86 2 225 950000 2 295.8 87 2 360 2362000 <2 246.4 88 2 300 1750000 2 270.5 89 2 239 1025800 <2 293.8 90 3 305 2363000 2 268.8 91 3 245 1700000 2 291.7 92 3 341 2362000 <2 255.3 93 3 281 1382000 2 277.2 94 3 220 2070000 2 295.2 95 4 287 2362000 <2 275.0 96 4 226 2362000 2 295.8 97 4 300 1382000 <2 270.5 98 4 239 2070000 - 293.8 99 5 305 2362000 2 268.8 100 5 245 2070000 2 291.7 101 5 341 2362000 <2 255.3 102 5 280 2362000 11 277.5 103 6 305 2070000 <2 268.8 104 6 245 1850000 2 291.7 105 6 341 1650000 2 255.3 106 6 280 1382000 3 277.5 107 6 219 1382000 <2 295.0 Tabella A-11 − Prova di fatica pannello P4.
N. Linea sald. X [mm] N d [mm] σScr(max) [MPa] 108 1 358 3582000 <2 218.8 109 1 297 1930000 2 240.2 110 1 236 1400700 2 260.6 111 2 340 4049000 <2 226.2
N. Linea sald. X [mm] N d [mm] σScr(max) [MPa] 114 3 360 4006600 2 217.9 115 3 300 2460000 3 239.3 116 3 240 3582000 <2 259.6 117 4 340 4006600 <2 226.2 118 4 280 3710000 <2 245.5 119 4 220 4006600 <2 261.1 120 1 345 3582000 <2 224.3 121 1 285 2769000 2.5 243.9 122 1 225 2769000 3 261.7 123 2 302 2769000 <2 238.7 124 2 242 2460000 <2 259.0 125 4 302 3159000 <2 238.7 126 4 242 3582000 2.5 259.0 127 5 285 3582000 <2 243.9 128 5 225 4049000 2 261.7 129 6 302 3159000 2.5 238.7 130 6 242 2880000 2 259.0 Tabella A-12 − Prova di fatica pannello P5.
N. Linea sald. X [mm] N N stimato d [mm] σScr(max) [MPa] 1 5 275 650000 650000 4 479.4 2 6 195 1067000 1067000 2 480.5 3 7 203 1067000 1067000 3.5 456.0 4 7 264 1067000 1067000 4.5 456.0 5 6 255 1067000 1000000 5 482.4 6 7 215 1067000 1000000 6.5 483.1 7 5 215 1067000 990000 7 446.5 8 7 273 1067000 990000 9 440.7 9 5 263 1067000 1067000 - 483.2 10 4 164 1660000 1660000 2 462.7 11 1 140 1660000 1660000 4 483.2 12 1 277 1660000 1660000 4 472.2 13 4 163 1660000 1600000 5 483.2 14 2 198 1660000 1600000 6 460.1 15 5 154 1660000 1600000 6 479.4 16 6 163 1660000 1600000 7 463.5 17 2 258 1660000 1500000 8 482.1 18 3 202 1660000 1500000 8 419.2 19 5 203 1660000 1500000 8 457.6 20 6 315 1660000 1500000 8 475.9 21 7 154 1660000 1500000 8 456.0 22 7 142 1660000 1500000 9 444.2 23 1 200 1660000 1400000 11 403.6 24 1 217 1660000 1400000 12 483.0 25 2 280 1660000 1400000 12 445.7
N. Linea sald. X [mm] N N stimato d [mm] σScr(max) [MPa] 27 6 163 1660000 1400000 13 417.2 28 4 224 1660000 1300000 18 412.8 29 4 254 1660000 1300000 18 419.2 30 2 220 1660000 1200000 20 442.8 31 3 275 1660000 1200000 20 412.8 32 1 262 1660000 1200000 21 419.2 33 4 284 1660000 1200000 22 401.9 34 3 262 1660000 1200000 23 478.1 35 6 223 1660000 1100000 31 419.8 Tabella A-13 − Prova di fatica pannello P6 (saldatura passante).